ZAMAK alloys were first developed during the 1920's by The New Jersey Zinc Company. The name ZAMAK draws upon the basic metallurgy of the alloy group: Z-Zinc, A-Aluminum, MA-Magnesium, and K-Kopper (e.g., German). In the United States, ZAMAK 3 is the most common alloy for hot chamber die casting. With a combination of superior mechanical properties and low melting/manufacturing costs, it fulfills the needs for most die casting applications. Other ZAMAK alloys include ZAMAK 2, ZAMAK 5, and ZAMAK 7. Common to each alloy is a consistent Aluminum content range, however, the alloys differ in specification by varying amounts of copper, magnesium, and nickel - resulting in different mechanical and physical properties.
锌合金的特点:
比重大。
铸造性能好，可以压铸形状复杂、薄壁的精密件，铸件表面光滑。
可进行表面处理：电镀、喷涂、喷漆。
熔化与压铸时不吸铁，不腐蚀压型，不粘模。
有很好的常温机械性能和耐磨性。
熔点低，在385℃熔化，容易压铸成型。
使用过程中须注意的问题：
(蚀性差)
当合金成分中杂质元素铅、镉、锡超过标准时，导致铸件老化而发生变形，表现为体积胀大，机械性
能特别是塑性显著下降，时间长了甚至破裂。铅、锡、镉在锌合金中溶解度很小，因而集中于晶粒边
界而成为阴极，富铝的固溶体成为阳极，在水蒸气（电解质）存在的条件下，促成晶间电化学腐蚀。
压铸件因晶间腐蚀而老化。
(时效作用)
锌合金的组织主要由含Al和Cu的富锌固溶体和含Zn的富Al固溶体所组成，它们的溶解度随温度的下降
而降低。但由于压铸件的凝固速度极快，因此到室温时，固溶体的溶解度是大大地饱和了。经过一定
时间之后，这种过饱和现象会逐渐解除，而使铸件地形状和尺寸略起变化。
(温度作用)
锌合金压铸件不宜在高温和低温（0℃以下）的工作环境下使用。锌合金在常温下有较好的机械性能。
但在高温下抗拉强度和低温下冲击性能都显著下降。
锌合金种类
Zamak 3:良好的流动性和机械性能。
应用于对机械强度要求不高的铸件，如玩具、灯具、装饰品、部分电器件。
Zamak 5: 良好的流动性和好的机械性能。
Zamak 2: 用于对机械性能有特殊要求、对硬度要求高、尺寸精度要求一般的机械零件。
ZA8: 良好的流动性和尺寸稳定性，但流动性较差。
应用于压铸尺寸小、精度和机械强度要求很高的工件，如电器件。
流动性最佳，应用于压铸薄壁、大尺寸、精度高、形状复杂的工件，如电器元件及其盒体。
不同的锌合金有不同的物理和机械特性，这样为压铸件设计提供了选择的空间。
Superloy: 流动性最佳，应用于压铸薄壁、大尺寸、精度高、形状复杂的工件，如电器元件及其盒
体。不同的锌合金有不同的物理和机械特性，这样为压铸件设计提供了选择的空间。.